Возможности клинического использования конструкций на основе диоксида циркония и оценка основных свойств нового керамического материала стоматологического назначения

Abstract

Every year, steadily increasing the quantity of patients, ortopedic treatment which is performed using structures made of zirconium dioxide. The interest of dentists to this method of replacing teeth and defects of dentition due to the fact that orthopedic constructions made of zirconium dioxide with the use of CAD I CAM technologies have high durability, aesthetics and precision. A method for the synthesis of nanocrystalline powder of Zr02, stabilizet with Y203, by co-deposition with the use of elements of the solgel technology for low temperature sintering. X-ray diffraction, thermal desorption of nitrogen, and electron microscopy study of powder characteristics, depending on synthesis conditions. Preclinical trials indicate the developed material meets the require ments of durability end aesthetics.

С каждым годом, неуклонно увеличивается число пациентов, ортопедическое лечение которых проводится с использованием конструкций выполненных из диоксида циркония. Интерес стоматологов к данному методу замещения дефектов зубов и зубных рядов обусловлен тем, что ортопедические конструкции, изготовленные из диоксида циркония с применением CAD/CAM технологий обладают высокой прочностью, эстетичностью и прецензионностью. Разработана методика синтеза нанокристаллического порошка Zr02, стабилизированного Y203, методом совместного осаждения с применением элементов золь-гель технологии, для низкотемпературного спекания. Методами рентгеновской дифракции, тепловой десорбции азота и электронной микроскопии изучены характеристики порошка в зависимости от условий синтеза. Проведенные доклинические испытания свидетельствуют, что разработанный материал отвечает требованиям прочности и эстетичности.